Product Details:
|
| Material: | Carbon Graphite | Application: | Machinery Industry,pump |
|---|---|---|---|
| Size: | Customized | Chemical Composition: | Carbon Graphite, Carbon>99% |
| Design: | OEM&ODM | Product Lead Time: | 25-30days |
| High Light: | OEM carbon graphite seal rings,machinery sealing carbon graphite seal rings |
||
High Quality Carbon Graphite Seal Rings For Machinery Sealing
Carbon graphite bushings are widely used in various applications, including pumps. These bushings are made from a combination of carbon and graphite materials, which are mixed and then molded into the desired shape.
Materials For Option
| Category | Model | Impregnant | Shore Hardess | Flexural Strength | Compressive Strength | Porosity | Bulk Density | Thermal expansion coeffcient | Temp. | |||
| ≥ | `X | ≥MPa | `X | ≥MPa | `X | ≤% | g/cm3 | 10-6/℃ | ℃ | |||
| Graphite | M120 | - | 60 | - | 25 | - | 81 | - | 18 | 1.6 | 4 | 350 |
| M154 | - | 40 | - | 20 | - | 40 | - | 28 | 1.42 | - | 350 | |
| M254 | - | 10 | - | 25 | - | 45 | - | 25 | 1.65 | 3.4 | 450 | |
| Impregnated resin carbon graphite | M106H | Epoxy resin | 75 | 90 | 51 | 60 | 180 | 190 | 1.0 | 1.62 | 4.8 | 200 |
| M238H | 40 | 55 | 39 | 50 | 78 | 110 | 1.0 | 1.85 | 4.5 | 250 | ||
| M255H | 40 | 50 | 34 | 45 | 78 | 90 | 1.0 | 1.8 | 4.5 | 200 | ||
| M106K | Furan resin | 80 | 95 | 55 | 65 | 200 | 210 | 2.0 | 1.62 | - | 200 | |
| M120K | 75 | 95 | 50 | 60 | 190 | 195 | 2.0 | 1.7 | 200 | |||
| M154K | 60 | 35 | 70 | 6.0 | 1.6 | 200 | ||||||
| M158K | 80 | 90 | 54 | 60 | 200 | 210 | 1.2 | 1.65 | - | 200 | ||
| Impregnated metal carbon graphite | M106D | Antimony alloy | 75 | - | 55 | 65 | 170 | 190 | 3 | 2.2 | 5.0 | 500 |
| M120D | 70 | - | 50 | 60 | 140 | 160 | 3 | 2.2 | 5.0 | 500 | ||
| M254D | 35 | - | 35 | - | 65 | - | 3 | 2.2 | 4.5 | 500 | ||
| M120P | Copper alloy | 65 | - | 65 | - | 200 | - | 3 | 2.4 | - | 400 | |
| Impregnated glass carbon graphite | M106R | Glass | 110 | - | 75 | - | 210 | - | 1.5 | 1.9 | 4.67 | 600 |
| M120R | 95 | - | 57 | - | 190 | - | 1.5 | 1.9 | 4.67 | 600 | ||
| M254R | 65 | - | 55 | - | 100 | - | 1.5 | 1.9 | - | 600 | ||
| M262R | 75 | - | 48 | - | 138 | - | 1.5 | 1.9 | - | 600 | ||
| Hot pressed graphite | M353 | - | 45 | - | 45 | - | 120 | - | 1.0 | 1.75 | - | 100 |
| M352 | - | 35 | - | 35 | - | 80 | - | 1.0 | 1.75 | - | 100 | |
| M356 | - | 50 | - | 50 | - | 140 | - | 1.0 | 1.75 | - | 100 | |
| M357 | - | 40 | - | 40 | - | 80 | - | 1.0 | 1.75 | 9.0 | 100 | |
Chemical Resistance Of Mechanical Carbon Grapshite Material
| Medium | Mass Fraction % | Pure Carbon Graphite | Impregnated Resin Carbon Graphite | Impregnated Metal Carbon Graphite | Hot Pressed Carbon Graphite | |||||
| Phenoic | Epoxy | Furan | Antimony | Babbitt Alloy | Aluminm Alloy | Copper Alloy | ||||
| Hydrochloric acid | 50 | + | 0 | + | 0 | ~ | ~ | ~ | ~ | 0 |
| Sulfuric acid | 50 | + | 0 | + | 0 | ~ | ~ | ~ | ~ | 0 |
| Sulfuric acid | 98 | + | 0 | ~ | + | ~ | ~ | ~ | ~ | 0 |
| Nitric acid | 50 | 0 | 0 | 0 | 0 | ~ | ~ | ~ | ~ | 0 |
| Nitric acid | concentrated | ~ | ~ | ~ | ~ | ~ | ~ | ~ | ~ | ~ |
| Acetic acid | 36 | + | + | ~ | 0 | ~ | 0 | 0 | 0 | 0 |
| Seawater | ~ | + | 0 | + | 0 | ~ | + | 0 | 0 | 0 |
| Benzene | 100 | + | + | 0 | + | + | + | + | + | + |
| Ammonia | 10 | + | 0 | + | + | + | + | + | ~ | 0 |
| Acetone | 100 | + | 0 | 0 | + | + | 0 | + | + | 0 |
| Urea | 70 | + | + | + | + | + | 0 | + | ~ | 0 |
| Motor oil | ~ | + | 0 | + | + | + | 0 | + | + | + |
| Gasoline | ~ | + | 0 | 0 | + | + | 0 | + | + | + |
| Remarks: | + is stable, 0 is normally, ~ is unstable | |||||||||